Product systems: Natural stone

MULTISTONE is a multi-functional light-weight tile adhesive for the fitting of almost all of almost all natural stones as well as ceramic wall and floor coverings in interior and exterior areas. Due to the airflow Technology MULTISTONE is particularly easy and smooth to handle.

• Highly stable and highly flexible
• Particularly well suited for large format sizes
• High yield (goes a long way)
• Rapid curing with crystalline water bonding

Bonding of:

• Natural stones


• vitreous stoneware and porcelain


• non-vitreous stoneware


• split tiles


• floor clinker tiles, clinker tiles and Cotto


• hand-made tiles


• small, medium and glass mosaics


• glass tiles


• insulation and lightweight building boards

Very smooth boards (e.g. rigid foam slabs) must be roughened up prior to bonding.

• concrete, lightweight concrete, and porous concrete


• joint full brickwork


• plasters of the mortar categories CS II, CS III and CS IV in accordance with DIN EN 998 and gypsum plaster in accordance with DIN EN 13279 (Compressive strength ≥ 2.5 N/mm²)


• BOTAMENT building boards


• old tiling


• gypsum walls, gypsum plaster boards and gypsum fibreboards


• cement screeds and calcium sulphate screeds

The substrate must be in the following condition:

• dry, clean and frost-free


• stable


• free from grease, paint, cement laitance, separating agents, sinter layers and loose particles

Absorbent substrates must be primed with BOTAMENT D 11.

cool and dry at least 9 months in its original sealed container

Mixing ratio S1:

levelling mortar = ~ 3.6 l of water/ 15 kg

thick-bed = ~ 3.6 l of water/ 15 kg

medium-bed = ~ 3.8 l of water/ 15 kg

thin-bed = ~ 4.5 l of water/ 15 kg

pourable bed = ~ 4.8 l of water/ 15 kg

Mixing ratio S2:

thin-bed = 3.75 l BOTAMENT® D 10 + 0.75 l water/15kg

pourable bed = 4.0 l BOTAMENT® D 10 + 0.8 l water /15kg

~ 3 minutes

~ 20 minutes

~ 30 minutes

30 mm

after ~ 3 hours

after ~ 48 hours

after ~ 3 hours

Mix up using cold, clean water while stirring with a slow rotating agitator until a homogenous, stiff and paste-like mass has formed

+ 5 °C to + 25 °C

Consumption thin-bed: 6 mm notched trowel = ~ 2.0 kg/m² 8 mm notched trowel = ~ 2.6 kg/m² 10 mm notched trowel = ~ 3.0 kg/m² Consumption medium-bed: ~ 4.0 kg/m² Consumption pourable bed: 8 mm notched trowel = ~ 2.5 kg/m² 10 mm notched trowel = ~ 2.8 kg/m²

When installing ceramic coverings all existing standards and guidelines in their current versions must be observed.